碳纖(xian)維(wei)布加(jia)固(gu)技術注意事項（簡明(ming)版）一、材料(liao)(liao)選擇(ze)與存儲1.選用(yong)認(ren)證(zheng)的碳纖(xian)維(wei)布及配(pei)套(tao)膠(jiao)粘劑，需(xu)提(ti)供材料(liao)(liao)檢測(ce)報告2.碳纖(xian)維(wei)布應(ying)(ying)避光保存于(yu)陰(yin)涼(liang)干(gan)燥處(chu)(chu)(chu)，環氧(yang)樹脂(zhi)膠(jiao)保質期(qi)一般為6-12個(ge)月二、基(ji)層(ceng)處(chu)(chu)(chu)理要(yao)求(qiu)1.混(hun)凝土(tu)基(ji)面(mian)須(xu)打磨至骨料(liao)(liao)外(wai)露(lu)，轉角(jiao)處(chu)(chu)(chu)倒角(jiao)半徑≥20mm2.表面(mian)清(qing)潔度(du)需(xu)達Sa2.5級，含水率≤6%，平(ping)整度(du)≤3mm/2m3.對裂縫寬度(du)≥0.2mm處(chu)(chu)(chu)需(xu)行(xing)封閉處(chu)(chu)(chu)理三、施(shi)工(gong)(gong)環境控制1.環境溫(wen)(wen)度(du)5-35℃，濕度(du)≤70%時施(shi)工(gong)(gong)2.雨天禁(jin)止(zhi)露(lu)天施(shi)工(gong)(gong)，冬季施(shi)工(gong)(gong)需(xu)采(cai)取加(jia)溫(wen)(wen)養護(hu)措施(shi)四、施(shi)工(gong)(gong)工(gong)(gong)藝要(yao)點1.按(an)設(she)計(ji)(ji)尺寸(cun)裁剪，搭接(jie)(jie)長度(du)≥100mm2.涂(tu)(tu)膠(jiao)厚(hou)度(du)1.5-2mm，確保浸漬完(wan)全(quan)無白絲3.滾(gun)壓應(ying)(ying)從中間向兩(liang)端排除氣泡，禁(jin)止(zhi)往(wang)復(fu)碾壓4.多層(ceng)粘貼時需(xu)待前層(ceng)固(gu)化(hua)至指干(gan)狀態(tai)（約2-4小(xiao)時）五、質量(liang)檢驗標準1.空鼓(gu)(gu)面(mian)積(ji)≤5%，單個(ge)空鼓(gu)(gu)≤100cm22.現(xian)場拉拔強度(du)≥2.5MPa且為混(hun)凝土(tu)內聚(ju)破壞3.碳纖(xian)維(wei)布實際粘貼量(liang)誤(wu)差(cha)≤±5%六、安全(quan)防(fang)護(hu)要(yao)求(qiu)1.操作人員(yuan)應(ying)(ying)配(pei)備(bei)防(fang)護(hu)手(shou)套(tao)、護(hu)目鏡及防(fang)毒面(mian)具2.施(shi)工(gong)(gong)現(xian)場保持(chi)通(tong)風(feng)，避免(mian)明(ming)火(huo)接(jie)(jie)觸環氧(yang)樹脂(zhi)3.廢棄膠(jiao)粘容器應(ying)(ying)集中處(chu)(chu)(chu)理，禁(jin)止(zhi)隨(sui)意傾倒七(qi)、后(hou)期(qi)維(wei)護(hu)管理1.固(gu)化(hua)期(qi)內（7天）避免(mian)振(zhen)動或沖擊荷載2.建議每2年進行(xing)定期(qi)檢查，重點監測(ce)空鼓(gu)(gu)、剝離(li)情況3.外(wai)露(lu)碳纖(xian)維(wei)布應(ying)(ying)做防(fang)火(huo)/UV防(fang)護(hu)處(chu)(chu)(chu)理（如抹灰層(ceng)或防(fang)火(huo)涂(tu)(tu)料(liao)(liao)）注：具體(ti)參數應(ying)(ying)根(gen)據設(she)計(ji)(ji)文(wen)件及《混(hun)凝土(tu)結構(gou)加(jia)固(gu)設(she)計(ji)(ji)規范(fan)》（GB50367）調整，施(shi)工(gong)(gong)前須(xu)進行(xing)工(gong)(gong)藝試驗驗證(zheng)。

房屋碳纖維加固技術介紹碳纖維加固技術是近年來廣泛應用于建筑結構加固的新型技術，通過將高強度碳纖維布或板材粘貼于混凝土、鋼結構等基材表面，顯著提升建筑物承載力、抗震性和耐久性。該技術因其性和便捷性，成為傳統加固方法的重要替代方案。材料特性：碳纖維復合材料具有強度高（抗拉強度達3400MPa以上）、重量輕（密度1.6g/cm3）、耐腐蝕性強等特點。其抗拉強度約為鋼材的10倍，而重量僅為鋼材的1/4，施工后幾乎不增加結構自重。配套使用的改性環氧樹脂膠粘劑兼具高粘結性和柔韌性，能有效傳遞應力。施工流程：1.基面處理：清除結構表面松散層并打磨平整2.涂刷底膠：增強基材與碳纖維的粘結力3.粘貼碳纖維布：按設計方向逐層鋪設并輥壓密實4.表面防護：涂抹防火/防腐面層保護材料技術優勢：1.施工周期短（約為傳統加固的1/3）2.不影響建筑外觀和使用空間3.適應復雜造型結構加固需求4.耐酸堿腐蝕，使用壽命可達50年以上應用范圍：?混凝土梁板柱承載力不足?老舊房屋抗震加固?結構裂縫修復?歷史建筑保護性加固?超負荷使用建筑改造注意事項：需由機構進行結構計算和方案設計，施工須符合《混凝土結構加固設計規范》（GB50367）。不適用于基材嚴重碳化（強度

粘(zhan)(zhan)貼(tie)碳(tan)(tan)纖(xian)維布加(jia)固(gu)(gu)工藝流程(cheng)**1.基(ji)(ji)(ji)層處(chu)(chu)(chu)理(li)**清(qing)除混凝土表(biao)面(mian)(mian)劣化(hua)層（剝落(luo)、蜂窩等），采(cai)用(yong)打磨機(ji)露出(chu)(chu)堅(jian)實基(ji)(ji)(ji)層，裂縫處(chu)(chu)(chu)需注(zhu)漿(jiang)封閉(bi)。轉角(jiao)部(bu)位(wei)打磨為圓(yuan)弧(hu)（R≥20mm），用(yong)壓(ya)縮空氣清(qing)理(li)粉(fen)塵(chen)，確(que)保基(ji)(ji)(ji)面(mian)(mian)干(gan)燥、平(ping)(ping)整(zheng)。**2.涂(tu)(tu)刷(shua)底膠**按(an)比例調配環氧(yang)樹脂底膠，均勻涂(tu)(tu)刷(shua)于(yu)處(chu)(chu)(chu)理(li)后(hou)的基(ji)(ji)(ji)面(mian)(mian)，厚(hou)度(du)0.2~0.3mm，膠體滲(shen)透至混凝土內部(bu)。底膠表(biao)干(gan)后(hou)（觸拉不粘(zhan)(zhan)手）進入下(xia)一工序，固(gu)(gu)化(hua)時(shi)間依環境溫濕度(du)調整(zheng)。**3.表(biao)面(mian)(mian)找(zhao)平(ping)(ping)**對凹凸不平(ping)(ping)處(chu)(chu)(chu)采(cai)用(yong)修補(bu)膠填補(bu)，刮平(ping)(ping)，確(que)保粘(zhan)(zhan)貼(tie)面(mian)(mian)平(ping)(ping)整(zheng)度(du)偏(pian)差≤3mm/2m。重點(dian)處(chu)(chu)(chu)理(li)蜂窩麻(ma)面(mian)(mian)及模板(ban)(ban)接縫部(bu)位(wei)。**4.粘(zhan)(zhan)貼(tie)碳(tan)(tan)纖(xian)維布**①**裁剪**：按(an)設計尺寸(cun)(cun)裁剪碳(tan)(tan)布，碳(tan)(tan)纖(xian)維布加(jia)固(gu)(gu)平(ping)(ping)多(duo)少錢，搭接長度(du)≥100mm（受力方(fang)(fang)(fang)向）或(huo)(huo)200mm（非受力方(fang)(fang)(fang)向）；②**浸(jin)膠**：將碳(tan)(tan)布平(ping)(ping)鋪于(yu)涂(tu)(tu)刷(shua)浸(jin)漬膠的基(ji)(ji)(ji)面(mian)(mian)上，采(cai)用(yong)滾(gun)刷(shua)沿纖(xian)維方(fang)(fang)(fang)向反復滾(gun)壓(ya)，排出(chu)(chu)氣泡，使膠液充分浸(jin)潤；③**多(duo)層粘(zhan)(zhan)貼(tie)**：首層固(gu)(gu)化(hua)后(hou)重復操作，相鄰層纖(xian)維方(fang)(fang)(fang)向交叉(cha)布置，間隔時(shi)間≤1小(xiao)時(shi)；④**端部(bu)錨固(gu)(gu)**：梁柱端部(bu)增(zeng)(zeng)設U型箍或(huo)(huo)鋼(gang)板(ban)(ban)機(ji)械(xie)錨固(gu)(gu)，防(fang)止(zhi)剝離(li)。**5.固(gu)(gu)化(hua)養護**施(shi)工后(hou)靜置固(gu)(gu)化(hua)，環境溫度(du)≥15℃時(shi)養護7天，期間避(bi)免(mian)擾動或(huo)(huo)荷載(zai)。采(cai)用(yong)錘擊法檢(jian)查空鼓率，單處(chu)(chu)(chu)空鼓面(mian)(mian)積＜100cm2且總(zong)占(zhan)比＜5%為合格。**6.防(fang)護處(chu)(chu)(chu)理(li)**根據需求涂(tu)(tu)刷(shua)防(fang)火(huo)涂(tu)(tu)料或(huo)(huo)抹20mm厚(hou)砂(sha)漿(jiang)保護層，避(bi)免(mian)紫(zi)外線直(zhi)射和機(ji)械(xie)損傷。**注(zhu)意事項(xiang)**：環境溫度(du)宜(yi)為5~35℃，濕度(du)≤70%；膠體須現配現用(yong)，初凝后(hou)禁用(yong)；施(shi)工全程(cheng)需記錄溫度(du)、濕度(du)及材料批號。該工藝通(tong)過碳(tan)(tan)纖(xian)維高強特性提升(sheng)結(jie)構(gou)承載(zai)力，適用(yong)于(yu)梁板(ban)(ban)抗彎、柱墻(qiang)抗震(zhen)加(jia)固(gu)(gu)，具有施(shi)工快(kuai)捷(jie)、不增(zeng)(zeng)加(jia)截面(mian)(mian)尺寸(cun)(cun)等優勢。